Semiconductor device having vertical channels and method of manufacturing the same

ABSTRACT

A method of manufacturing a semiconductor device which can prevent leakage current caused by gate electrodes intersecting element isolation layers in a major axis of an active region, and which further has vertical channels to provide a sufficient overlap margin, and a semiconductor device manufactured using the above method. The device includes gate electrodes formed on element isolation layers that are disposed between active regions and have top surfaces that are higher than the top surfaces of the active regions. Since the gate electrodes are formed on the element isolation layers, leakage current in a semiconductor substrate is prevented. In addition, the gate electrodes are formed using a striped shape mask pattern, thereby obtaining a sufficient overlap margin compared to a contact shape or bar shape pattern.

CROSS-REFERENCE TO RELATED PATENT APPLICATION

This application claims the benefit of Korean Patent Application No. 10-2005-0064067, filed on Jul. 15, 2005, in the Korean Intellectual Property Office, the disclosure of which is incorporated herein in its entirety by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a semiconductor device and a method of manufacturing the same, and more particularly, to a semiconductor device having vertical channels and a method of manufacturing the same.

2. Description of the Related Art

As the length of a channel in a semiconductor device, for example, a field effect transistor (FET), decreases, several characteristics of the FET degrade. For example, short channel effects such as punch-through, drain induced barrier lowering (DIBL), and sub-threshold voltage swing occur. In addition, there are other problems such as an increase in parasitic capacitance (contact capacitance) between a contact region and a substrate, and an increase in leakage current.

In a FET including an active region having vertical channels on a semiconductor substrate, at least one side surface of a fin is used as a channel. A short channel effect can be prevented by an increase in the length of the channel, thereby improving current characteristics. Hereinafter, an active region having a vertical channel is referred to as a fin, and a FET having a fin is referred to as a fin-FET.

FIG. 1A is a plan view of a conventional fin-FET. FIG. 1B is a cross-sectional view of the conventional fin-FET taken along line 1B-1B of FIG. 1.

Referring to FIGS. 1A and 1B, an element isolation layer 20 which defines an active region 12 having vertical channels is formed on a semiconductor substrate 10. A gate electrode 16 covers the active region 12, an element isolation layer 21 is disposed along a minor axis of the active region 12, and an element isolation layer 22 is disposed along a major axis of the active region 12. For convenience, the gate electrodes 16 can be divided into a gate electrode 16 a intersecting the active region 12 and a gate electrode 16 b intersecting the element isolation layer 22 disposed along the major axis of the active region 12. Reference numeral 18 is an interlayer insulation layer including the gate electrode 16 therein.

The gate electrode 16 b intersecting the element isolation layer 22 disposed along the major axis of the active region 12 contacts the sidewall of the active region 12 and is buried in the element isolation layer 22. When electric power is supplied to the buried gate electrode 16 b, leakage current is generated in adjacent portions of the active region 12, i.e., portions “a” of the active region 12. The leakage current degrades the refresh characteristics of the memory device.

Fin-FETs in which the gate electrode 16 b is not found on the element isolation layer 22 are disclosed are U.S. Pat. No. 6,396,108 and U.S. Pat. No. 6,583,469. In these disclosures, to prevent the formation of the gate electrode 16 on the element isolation layer 22, the gate electrode 16 has a contact shape or bar shape, and thus the gate electrode 16 cannot be formed on the element isolation layer 22 disposed along the major axis of the active region 12.

However, as the design rule decreases, it becomes difficult to form a contact shape or bar shape gate electrode pattern on a substrate. In particular, it is difficult to obtain an overlap margin during a photolithography process in which the gate electrode pattern is formed.

SUMMARY

The present invention provides a method of manufacturing a semiconductor device having vertical channels that can prevent leakage current caused by a gate electrode intersecting an element isolation layer extending along a major axis of an active region, and provide a sufficient overlap margin. The present invention also provides a semiconductor device manufactured using the above method.

According to an embodiment of the present invention, there is provided a method of manufacturing a semiconductor device having vertical channels, the method including: etching a semiconductor substrate to protrude a plurality of active regions that are adjacent to each other, forming filling material layers in element isolation regions by filling etched portions between the active regions, and forming a first mask pattern that extends in a first direction and covers at least a portion between adjacent active regions. In addition the method also includes forming a second mask pattern to extend in a second direction at a predetermined angle with respect to the first direction, removing an exposed portion of the filling material layers using the first and second mask patterns as etching masks, removing the first and second mask patterns, exposing the active regions disposed between the filling material layers, and forming gate electrodes on the exposed active regions.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other features and advantages of the present invention will become more apparent by describing in detail exemplary embodiments thereof with reference to the attached drawings in which:

FIG. 1A is a plan view of a conventional fin-FET;

FIG. 1B is a cross-sectional view taken along line 1B-1B of FIG. 1;

FIGS. 2A through 8A are plan views illustrating a method of forming a fin-FET according to an embodiment of the present invention;

FIGS. 2B through 6B are cross-sectional views illustrating the method of FIGS. 2A through 6A, respectively, taken along line A-A of FIG. 2A;

FIGS. 2C through 8C are cross-sectional views illustrating the method of FIGS. 2A through 8A, respectively, taken along line B-B of FIG. 2A;

FIGS. 2D through 8D are cross-sectional views illustrating the method of FIGS. 2A through 8A, respectively, taken along line C-C of FIG. 2A;

FIGS. 7B and 8B are cross-sectional views illustrating the method of FIGS. 7A and 8A, respectively, taken along line A′-A′ of FIG. 2A;

FIGS. 9A and 10A are plan views illustrating a method of forming a fin-FET according to another embodiment of the present invention;

FIGS. 9B and 10B are cross-sectional views illustrating the method of FIGS. 9A and 10A, respectively, taken along line A′-A′ of FIG. 2A;

FIGS. 9C and 10C are cross-sectional views illustrating the method of FIGS. 9A and 10A, respectively, taken along line B-B of FIG. 2A; and

FIGS. 9D and 10D are cross-sectional views illustrating the method of FIGS. 9A and 10A, respectively, taken along line C-C of FIG. 2A.

DETAILED DESCRIPTION

Hereinafter, the present invention will be described more fully with reference to the accompanying drawings, in which exemplary embodiments of the invention are shown. The invention may, however, be embodied in many different forms and should not be construed as being limited to the embodiments set forth herein; rather, these embodiments are provided so that this disclosure will be through and complete, and will fully convey the concept of the invention to those skilled in the art. In the drawings, like reference numerals denote like elements, and the sizes and thicknesses of layers and regions are exaggerated for clarity. It will also be understood that when a layer is referred to as being “on” another layer or substrate, it can be directly on the other layer or substrate, or intervening layers may also be present. In the descriptions, like reference numerals denote like elements.

In some embodiments of the present invention, a gate electrode is formed on an element isolation layer disposed along a major axis of an active region in a fin-FET using a line shaped mask pattern. The bottom portion of the gate electrode is filled with filling material layer, thereby preventing leakage current in a semiconductor substrate due to the gate electrode.

In some embodiments of the present invention, the gate electrode is formed using a damascene process. In addition, a fin-FET according to an embodiment of the present invention may have a double gate electrode formed using the damascene process or having a triple gate electrode formed using the damascene process.

FIGS. 2A through 8A are plan views illustrating a method of forming a fin-FET according to an embodiment of the present invention. FIGS. 2B through 6B are cross-sectional views illustrating the method of FIGS. 2A through 6A, respectively, taken along line A-A of FIG. 2A. FIGS. 7B and 8B are cross-sectional views illustrating the methods of FIGS. 7A and 8A, respectively, taken along line A′-A′ of FIG. 2A. FIGS. 2C through 8C are cross-sectional views illustrating the method of FIGS. 2A through 8A, respectively, taken along line B-B of FIG. 2A. FIGS. 2D through 8D are cross-sectional views illustrating the method of FIGS. 2A through 8A, respectively, taken along line C-C of FIG. 2A.

Referring to FIGS. 2A through 2D, a device isolation layer or an element isolation layer 112, which defines an active region 102 having vertical channels, is formed on a semiconductor substrate 100. In a method of forming the element isolation layer 112, mask layer 105, defining the element isolation layer 112 and each including a pad oxide layer 104 and a pad nitride layer 106, are formed on the semiconductor substrate 100 using a conventional photolithography process. The pad oxide layers 104 are formed to reduce stress between the substrate 100 and the pad nitride layers 106, and may have a thickness of about 20 to about 200 Å, and preferably about 100 Å. The pad nitride layers 106 are used as a hard mask when etching to form a recessed region 113 and is deposited to a thickness of about 500 to about 2,000 Å, and preferably about 800 to about 850 Å. The deposition method for the pad nitride layers 106 may be a conventional method, such as chemical vapor deposition (CVD), sub-atmospheric CVD (SACVD), low pressure CVD (LPCVD), or plasma enhanced CVD (PECVD).

The semiconductor substrate 100 is exposed using an anisotropic dry etching method. The semiconductor substrate 100 is then etched to a predetermined depth using the mask layers 105 as an etching mask to form recessed regions 113. A photoresist pattern (not illustrated) is removed using conventional methods, such as ashing using oxygen plasma or organic stripping. The recessed region 113 is formed to a sufficient depth to isolate elements. Next, sidewall oxide layers 108 are formed on the entire surface of the recessed region 113. The sidewall oxide layers 108 are formed on the inner walls and bottom of the recessed region 113 to compensate for the damage caused during the etching process used in forming the recessed region 113. The sidewall oxide layer 108 is a thermal oxide layer or a CVD oxide layer, and may have a thickness of about 20 to about 200 Å.

Next, a nitride layer liner 110 covering the sidewall oxide layer 108 and the exposed mask layer 105 is deposited. The nitride layer liner 110 may be formed along the inner surfaces of the recessed region 113. The nitride layer liner 110 prevents oxidization of the sidewall oxide layer 108 in subsequent processes and improves the insulating characteristics of a later formed element isolation layer. The nitride layer liner 110 is formed to a thickness of about 50 to about 300 Å using CVD. A capping layer (not illustrated) may be formed on the nitride layer liner 110. The capping layer prevents damage to the nitride layer liner 110 in subsequent processes and may be formed of middle temperature oxide (MTO).

The forming of the nitride layer liner 110 can be omitted, if desired. In addition, the pad nitride layers 106 may be removed, or may remain to prevent damage to the active regions 102 in subsequent processes.

The recessed regions 113 are filled with a filling material layer. The filling material layer is an insulation layer and may be chosen from an undoped silicate glass (USG) layer, an high-density plasma (HDP) oxide layer, a tetraethylorthosiliate (TEOS) layer formed using PECVD, and an oxide layer formed using PECVD. The HDP oxide layer, which is a thin layer, may be the most suitable for reclaiming the recessed regions 113. The HDP CVD process may be a combination of a CVD process and an etching process using sputtering. In the HDP CVD process, a depositing gas for depositing a material layer and a sputtering gas with which a deposited material layer is etched via sputtering are supplied into a chamber. In an embodiment of the present invention, SiH₄ and O₂ are supplied into the chamber as depositing gases and an inert gas, such as an argon gas, is supplied into the chamber as the sputtering gas. Some of the supplied depositing gas and sputtering gas is ionized by plasma induced by high frequency electric power in the chamber. Biased high frequency electric power is supplied to a wafer chuck, i.e., an electrostatic chuck, in the chamber where the substrate is loaded, thus accelerating the ionized depositing gas and sputtering gas to the surface of the substrate. The accelerated depositing gas ions form a silicon oxide layer, and the accelerated sputtering gas ions sputter the deposited silicon oxide layer. Therefore, the element isolation layer 112 formed of HDP oxide is thin and has good gap fill characteristics.

The recessed region 113 filled with the filling material layer is then planarized until the top surface of the nitride layer liner 110 is exposed to form the element isolation layer 112. The planarization process may be performed using chemical mechanical polishing (CMP) or an etch-back process. In the planarization process, the nitride layer liner 110 is used as a planarization stopper. For example, when the planarization process is performed using CMP, the nitride layer liner 110 acts as a CMP stopper. A slurry used during CMP may etch the element isolation layers 112, for example, the HDP oxide layer, faster than the nitride layer liner 110. Accordingly, a slurry including a seria group abrasive may be used.

Referring to FIGS. 3A through 3D, a first mask pattern 114 covering the major axis of the active region 102 is formed. The first mask pattern 114 may cover first element isolation layers 120 (see FIG. 7A) between the adjacent active regions 102 along the direction of the major axis of the active region. The first mask pattern 114 may be arranged in stripes. To form the first mask pattern 114, a mask material layer is formed on the element isolation layer 112 and the active regions 102. Next, a photoresist pattern (not illustrated) defining the first mask pattern 114 covering the major axis of the active region 102 is defined. The mask material layer is etched in the shape of the photoresist pattern to form the first mask pattern 114.

The first mask pattern 114 is used as a hard mask for forming gate electrodes and has a sufficient etch selectivity to the element isolation layer 112. For example, if the element isolation layer 112 is a silicon oxide layer, the first mask pattern 114 may be a silicon nitride layer. The first mask pattern 114, e.g., the silicon nitride layer, may be deposited to a thickness of about 2,000 to about 6,000 Å, and preferably about 3,500 to about 4,500 Å. The deposition method may be a conventional method, for example, CVD, SACVD, LPCVD, or PECVD.

The width of the first mask pattern 114 is equal to or less than the width of the active region 102. For example, the width of the first mask pattern 114 may be about 1 to about 15 nm less than the width of the active region 102, and preferably about 3 to about 8 nm less than the width of the active region 102, thereby enhancing an overlap. However, when the width of the first mask pattern 114 is less than this, a portion of the first element isolation region 120 along the major axis of the active region 102 may be etched. To prevent a portion of the first element isolation region 120 from being etched, auxiliary patterns may be further formed to correspond to the first element isolation layer 120 on both sides of a portion of a reticle used to form the first mask pattern 114.

Although not illustrated in detail in the drawings, the first mask pattern 114 may be formed from one end of a plurality of the active regions 102 to another end of a plurality of the active regions 102. For example, the arrangement of the plurality of the active regions 102 may be continuous from one end to another end of a cell region.

The process margin of the first mask pattern 114 having a line shape for forming a gate electrode is greater than the process margin of a mask pattern with a contact shape or a bar shape. Due to the large process margin, greater integration can be obtained, and thus the wavelength of the light source of a light emitting apparatus can be increased or a light emitting apparatus having a conventional light source and the number of apertures can be used without increasing the number of apertures. Accordingly, the first mask pattern 114 having a line shape can be efficiently applied to the formation of a fine pattern. In addition, the first mask pattern 114 having a line shape can prevent the generation of striation during the formation of the gate electrode, and thus an additional hard mask for removing the striation is unnecessary.

Referring to FIGS. 4A through 4D, filling layers 116 are formed on the element isolation layer 112 to fill the space between the first mask patterns 114, if desired. Each of the filling layers 116 may be an insulation layer chosen from an USG layer, an HDP oxide layer, a TEOS layer formed using PECVD, and an oxide layer formed using PECVD. However, since the element isolation layers 112 and the filling layers 116 may be simultaneously removed in a subsequent process, the element isolation layers 112 and the filling layers 116 may be formed of substantially the same material. For example, the element isolation layers 112 and the filling layers 116 may both be HDP oxide layers.

The filling layers 116 are planarized to the top surface of the first mask pattern 114. The planarization process is performed using CMP or an etch-back process. In the planarization process, the first mask pattern 114 is used as a planarization stopper layer. For example, when the filling layers 116 are planarized using the CMP, the first mask pattern 114 acts as a CMP stopper. A slurry used during the CMP may etch the filling layers 116, for example, the HDP oxide layer, faster than the first mask pattern 114. A slurry including a seria group abrasive may be used. Here, the filling layers 116 are used for the planarization, and thus are optionally formed.

Referring to FIGS. 5A through 5D, a second mask pattern 118, i.e., a photoresist pattern, is formed. The second mask pattern 118 extends at a predetermined transverse angle, for example, a right angle or an acute angle, with respect to the major axis of the active region 102, and includes stripes separated from each other by a predetermined distance. The second mask pattern 118 exposes portions of top surfaces of the filling layers 116 and portions of the first mask pattern 114.

Referring to FIGS. 6A through 6D, portions of the element isolation layers 112 along the minor axis of the active regions 102 are removed using the second mask pattern 118 and the first mask pattern 114 as an etching mask to form second element isolation layers 122. That is, portions of the filling layers 116 and the element isolation layers 112 disposed along the minor axis of the active regions 102 are removed by wet etching. For example, when the element isolation layers 112 and the filling layers 116 are HDP oxide layers, they can be removed using a buffered oxide etchant (BOE), which is a mixed solution of diluted HF, NH₄F, or HF and ionized water.

In an embodiment of the present invention, a first direction is defined along a major axis of the active region, for example, a direction in which line B-B of FIG. 2A extends. A first element isolation region 120 (FIG. 6C) disposed between the active regions extends along the first direction. A second direction may be a minor axis of the active region, for example, a direction in which line A-A of FIG. 2A extends. An element isolation region disposed between active regions extends along the second direction. In other words, the element isolation region extending along the second direction may be an element isolation region disposed in a region in which the line C-C of FIG. 2A extends. The element isolation region extending along the second direction can be divided into a second embodiment isolation region 122 which is recessed and a third element isolation region 124 which is not recessed. Thus, the element isolation layer may be divided into the first, second, and third element isolation regions (120, 122 and 124 respectively of FIGS. 6B, 6C and 6D) for convenience of explanation and ease of understanding, not for limiting the scope of the present invention.

Here, the degree to which the element isolation layers 112 are removed determines the channel lengths of the fin-FET according to this embodiment of the present invention. The recess depth is sufficient to isolate the adjacent active regions 102. As a result of the etching, a first element isolation layer 120 is formed between the active regions 102 along the first direction, and recessed second element isolation layers 122 and unrecessed third element isolation layers 124 are alternatively disposed along the second direction.

Referring to FIGS. 7A through 7D, the active regions 102 disposed between the second element isolation layers 122 are exposed. Specifically, the first mask pattern 114, the nitride layer liner 110, the mask layers 105, and the sidewall oxide layers 108, which cover the active regions 102, are removed. The exposure of the active regions 102 includes three operations because the nitride layer liners 110 disposed between the second element isolation layers 122 and the active regions 102 may be damaged in the processes of removing several layers, resulting in the generation of humps. A hump can generate leakage current and thus degrade current characteristics.

First, the first mask pattern 114, the nitride layer liner 110, and the pad nitride layers 106 disposed on the active regions 102 are removed by anisotropic dry etching. The nitride layers, i.e., the first mask pattern 114, the nitride layer liners 110, and the pad nitride layers 106, can be removed using a fluoride carbon group gas such as a C_(x)F_(y) group gas and a C_(a)H_(b)F_(c) group gas, for example, CF₄, CHF₃, C₂F₆, C₄F₈, CH₂F₂, CH₃F, CH₄, C₂H₂, C₄F₆, or a combination thereof. Argon gas may be used as an environmental gas.

Second, the portions of the nitride layer liner 110 remaining on the sidewalls of the active regions 102 are removed by isotropic wet etching using H₃PO₄. Third, the sidewall oxide layers 108 and the pad oxide layers 104 are removed by isotropic wet etching. Here, a BOE including a mixed solution of diluted HF, NH₄F, or HF and ionized water may be used as an etching solution.

When the surfaces of the active regions 102 are exposed, gate insulation layers 126 covering the active regions 102 are formed. The gate insulation layer 126 may be a silicon oxide layer, a hafnium oxide layer, a zirconium oxide layer, an aluminum oxide layer, a tantalum oxide layer, or a lanthanum oxide layer, which is deposited using CVD or ALD.

Referring to FIGS. 8 a and 8D, gate electrodes 128 which fill the recessed regions on the second element isolation layers 122 and cover portions of the active regions 102 and the first element isolation layers 120 are formed. Specifically, the gate electrodes 128 are deposited to fill the spaces above the second element isolation layers 122 and completely cover the top surface. The gate electrodes 128 are patterned using conventional photolithography so as to extend at a predetermined angle, for example, a right angle or an acute angle, with respect to the major axis of the active region 102, and are separated from each other by a predetermined distance. The gate electrodes 128 are electrically insulated from each other by interlayer insulation layers 130. The gate electrodes 128 may have the same 2-dimensional shape as the second mask patterns 118 in FIG. 5.

The gate electrodes 128 according to this embodiment of the present invention are formed using a damascene process. Accordingly, an overlap margin required to form the gate electrodes 128 is sufficient. That is, the gate electrodes 128 fill the spaces above the second element isolation layer 122 and cover the top surface and both side surfaces of the active regions 102. The fin-FET according to the first embodiment of the present invention has a triple gate structure in which the gate electrodes 128 cover the top surface and both side surfaces of the active regions 102.

Each of the gate electrodes 128 may include a polysilicon layer, a silicide layer, and a capping insulation layer sequentially stacked. However, instead of the polysilicon layer, a monolayer or a multilayer composed of amorphous silicon, poly Si-Ge, and/or a material including metal can be used. The material including metal may include a metal such as tungsten or molybdenum or may include a conductive metal nitride, such as titanium nitride, tantalum nitride, or tungsten nitride. The silicide layer may or may not be included. The capping insulation layer may comprise a material having a sufficient etch selectivity to an interlayer insulation layer which is deposited in a subsequent process, and may be, for example, a silicon nitride layer.

For convenience, the gate electrodes 128 can be divided into first electrodes 128 a intersecting the active regions 102 and second electrodes 128 b intersecting the first element isolation layer 120 disposed along the first direction. The top surfaces of the first element isolation layers 120 are at the same level or higher than the top surfaces of the active regions 102. The second electrodes 128 b are disposed on the first element isolation layers 120, and thus the generation of leakage current in the semiconductor substrate 100 due to the electric power supplied to the second electrodes 128 b can be prevented because the electric field formed by the second electrodes 128 b is blocked by the first element isolation layers 120. Meanwhile, both ends of the second electrodes 128 b are connected to the gate electrodes disposed on the second element isolation layers 122 to be extended.

FIGS. 9A and 10A are plan views illustrating a method of forming a fin-FET according to another embodiment of the present invention. FIGS. 9B and 10B are cross-sectional views illustrating the method of FIGS. 9A and 10A, respectively, taken along line A′-A′ of FIG. 2A. FIGS. 9C and 10C are cross-sectional views illustrating the method of FIGS. 9A and 10A, respectively, taken along line B-B of FIG. 2A. FIGS. 9D and 10D are cross-sectional views illustrating the method of FIGS. 9A and 10A, respectively, taken along line C-C of FIG. 2A.

Since the defining of the active region 102 and the forming of the first mask pattern 114 is the same as in the first embodiment as illustrated in FIGS. 2A through 6D, a description thereof will not be provided for the present embodiment.

Referring to FIGS. 9A through 9D, the active regions 102 disposed between the second element isolation layers 122 are exposed. Specifically, the first mask pattern 114, the nitride layer liner 110, portions of the pad nitride layers 106, and the sidewall oxide layers 108 which cover the active regions 102 are removed. The exposure of the active region 102 includes three operations because the nitride layer liners 110 disposed between the second element isolation layers 122 and the active regions 102 may be damaged in the process of removing several layers, resulting in the generation of humps. The hump can generate leakage current and thus degrade current characteristics.

First, the first mask pattern 114 and the nitride layer liner 110 disposed on the active regions 102 are removed by anisotropic dry etching. The nitride layers, i.e., the first mask pattern 114 and the nitride layer liner 110, can be removed using a fluoride carbon group gas such as C_(x)F_(y) group gas and a C_(a)H_(b)F_(c) group gas, for example, CF₄, CHF₃, C₂F₆, C₄F₈, CH₂F₂, CH₃F, CH₄, C₂H₂, C₄F₆, or a combination thereof. Argon gas may be used as an environmental gas. The mask layer 105 may not be etched, or the upper portion of the mask layer 105 may be etched to a predetermined height.

Second, portions of the nitride layer liner 110 remaining on the sidewalls of the active regions 102 are removed by isotropic wet etching using H₃PO₄. Third, the sidewall oxide layers 108 and the pad oxide layers 104 are removed by isotropic wet etching. Here, a BOE being a mixed solution of diluted HF, NH₄F, or HF and ionized water may be used as an etching solution.

When the side surfaces of the active regions 102 are exposed, gate insulation layers 226 are formed to cover the active regions 102 and mask layers 105, including the residual pad nitride layers. The gate insulation layer 226 may be a silicon oxide layer, a hafnium oxide layer, a zirconium oxide layer, an aluminum oxide layer, a tantalum oxide layer, or a lanthanum oxide layer deposited using CVD or ALD.

Referring to FIGS. 10A through 10D, gate electrodes 128 which fill the recessed regions on the second element isolation layers 122 and cover portions of the active regions 102 and the first element isolation layers 120 are formed. Specifically, the gate electrodes 128 are deposited to fill the spaces above the second element isolation layers 122 and to completely cover the top surface. The gate electrodes 128 are patterned using conventional photolithography so as to extend at a predetermined angle, for example a right angle or an acute angle, with respect to the major axis of the active region 102, and are separated from each other by a predetermined distance. The gate electrodes 128 are electrically insulated from each other by interlayer insulation layers 230. The gate electrodes 128 may have the same 2-dimensional shape as the second mask pattern 118 shown in FIG. 5.

The gate electrodes 128 according to the second embodiment of the present invention are formed using a damascene process. Accordingly, an overlap margin required to form the gate electrodes 128 is sufficient. That is, the gate electrodes 128 fill the spaces above the second element isolation layer 122 and cover both side surfaces of the active regions 102. The fin-FET according to the second embodiment of the present invention has a double gate structure in which the gate electrodes 128 cover both sides of the active regions 102.

Each of the gate electrodes 128 may include a polysilicon layer, a silicide layer, and a capping insulation layer sequentially stacked. However, instead of the polysilicon layer, a monolayer of a multilayer composed of amorphous silicon, poly Si-Ge, and/or a material including metal can be used. The material including metal may include a metal such as tungsten or molybdenum or may include a conductive metal nitride, such as titanium nitride, tantalum nitride, or tungsten nitride. The silicide layer may or may not be included. The capping insulation layer may be formed of a material having a sufficient etch selectivity to an interlayer insulation layer which is deposited in a subsequent process, and may be, for example, a silicon nitride layer.

For convenience, the gate electrodes 128 can be divided into first electrodes 128 a intersecting the active regions 102 and the second electrodes 128 b intersecting the first element isolation layer 120 disposed along the first direction. The top surfaces of the first element isolation layers 120 are at the same level or higher than the top surface of the active regions 102. The second electrodes 128 b are disposed on the first element isolation layers 120, and thus the generation of leakage current in the semiconductor substrate 100 due to the electric power supplied to the second electrodes 128 b can be prevented because the electric field produced by the second electrodes 128 b is blocked by the first element isolation layers 120. Meanwhile, both ends of the second electrodes 128 b are connected to the gate electrodes disposed on the second element isolation layers 122 to be extended.

The method of manufacturing a semiconductor device having a vertical channels according to the present invention can prevent the generation of leakage current in the semiconductor substrate since gate electrodes are formed on element on element isolation layers which extend upward to the same level or higher than the top surfaces of active regions.

In addition, in the method of manufacturing a semiconductor device having vertical channels according to the present invention, gate electrodes are formed using a line shape mask pattern, thereby obtaining a sufficient overlap margin.

In addition, the gate electrode is manufactured using a damascene process, thereby significantly increasing an overlap margin.

While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it will be understood by those of ordinary skill in the art that various changes in form and details may be made therein without departing from the spirit and scope of the present invention as defined by the following claims. 

1. A method of manufacturing a semiconductor device having vertical channels, the method comprising: etching a semiconductor substrate to protrude a plurality of active regions which are adjacent to each other; forming filling material layers in element isolation regions by filling etched portions between the active regions; forming a first mask pattern that extends in a first direction and covers at least a portion between adjacent active regions; forming a second mask pattern which extends in a second direction at a predetermined angle with respect to the first direction; removing an exposed portion of the filling material layers using the first and second mask patterns as etching masks; removing the first and second mask patterns; exposing the active regions disposed between the filling material layers; and forming gate electrodes on exposed active regions.
 2. The method of claim 1, wherein the forming of the filling material layers in the element isolation regions comprises: forming on the semiconductor substrate a mask layer including a pad oxide layer and a pad nitride layer which define the element isolation regions; forming recessed regions by anisotropic dry etching of the semiconductor substrate to a predetermined depth using the mask layer as an etching mask; forming sidewall oxide layers on sidewalls of the recessed regions; filling the recessed regions with the filling material layers; and planarizing the filling material layers until the pad nitride layer is exposed.
 3. The method of claim 2, further comprising: forming a nitride layer liner which covers exposed portions of the sidewall oxide layers and the mask layer before filling the recessed regions.
 4. The method of claim 1, wherein the first mask pattern is arranged in a striped pattern.
 5. The method of claim 1, wherein forming the first mask pattern comprises: forming mask material layers on the element isolation layers and the active regions; defining a photoresist pattern which defines the first mask pattern; and etching the mask material layers according to the shape of the photoresist pattern.
 6. The method of claim 5, wherein the thickness of the first mask pattern is about 2,000 Å to about 6,000 Å.
 7. The method of claim 5, wherein a portion of the first mask pattern remaining on an active region has a width equal to or less than the width of the active region.
 8. The method of claim 7, wherein the width of the portion of the first mask pattern is about 1 nm to about 15 nm less than the width of the active region.
 9. The method of claim 7, wherein the width of the portion of the first mask pattern is about 3 nm to about 8 nm less than the width of the active region.
 10. The method of claim 9, wherein auxiliary patterns are formed on both sides of a reticle corresponding to a first element isolation layer in the reticle for the exposure used to form the first mask pattern.
 11. The method of claim 5, wherein the first mask pattern extends from one end of a plurality of the active regions to another end of the plurality of the active regions.
 12. The method of claim 1, wherein the filling material layers have an etch selectivity with respect to the first mask pattern.
 13. The method of claim 1, wherein the filling material layers include silicon oxide layers and wherein the first mask pattern includes a silicon nitride layer.
 14. The method of claim 1, wherein the first direction extends substantially parallel to the major axis of the active regions.
 15. The method of claim 1, wherein the second direction extends substantially parallel to the minor axis of the active regions.
 16. The method of claim 1, wherein removing an exposed portion of the filling material layer comprises: filling the element isolation regions disposed between the first mask pattern with filling layers; planarizing the filling layers to expose the first mask pattern; forming a second mask pattern over the first mask pattern to expose portions of the top surfaces of the filling layers and a portion of the first mask pattern; and removing portions of the filling layers and the filling material layers using the first and second mask patterns as etching masks.
 17. The method of claim 16, wherein the filling layers are formed of the same material as the filling material layers.
 18. The method of claim 17, wherein the filling material layers and the filling layers include high-density plasma (HDP) oxide layers.
 19. The method of claim 1, wherein the degree of the removal of the filling material layers determines the lengths of the vertical channels.
 20. The method of claim 1, wherein recessed regions formed by the removal of the filling material layers have a sufficient depth to isolate adjacent active regions.
 21. The method of claim 1 further comprising forming gate insulation layers which cover at least two side surfaces of the exposed active regions, after removing the exposed portion of the filling material layers.
 22. The method of claim 3, wherein exposing the active regions comprises: removing the first mask pattern, a portion of the nitride layer liner, and the pad nitride layers disposed on the top surfaces of the active regions by anisotropic dry etching; removing a portion of the nitride layer liner remaining on the sidewalls of the active regions by isotropic wet etching; and removing the sidewall oxide layers and the pad oxide layers by isotropic wet etching.
 23. The method of claim 22 further comprising forming gate insulation layers which cover the top and side surfaces of the exposed active regions, after exposing the active regions.
 24. The method of claim 3, wherein the exposing of the active region comprises: removing the first mask pattern, a portion of the nitride layer liner, and portions of the pad nitride layers disposed on the top surface of the active regions by anisotropic dry etching; removing a portion of the nitride layer liner remaining on the sidewalls of the active regions by isotropic wet etching; and removing the sidewall oxide layers by isotropic wet etching.
 25. The method of claim 24 further comprising forming gate insulation layers which cover the side surfaces of the exposed active regions and residual pad nitride layers, after exposing the active regions.
 26. A semiconductor device having vertical channels, the device comprising: a plurality of active regions protruded from a top surface of the semiconductor substrate; first element isolation layers which separate adjacent active regions, the first isolation layers extending in a first direction and having top surfaces that are higher than at least the top surfaces of the active regions; second element isolation layers which extend at a predetermined angle with respect to the first direction, separate the adjacent active regions, and have top surfaces lower than the top surfaces of the active regions so as to expose at least a portion of the sidewalls of the active regions such that vertical channels can be formed; and gate electrodes formed on the first element isolation layers.
 27. The semiconductor device of claim 26 further comprising a nitride layer liner formed between the second element isolation layers and the active regions.
 28. The semiconductor device of claim 26, wherein the first and second element isolation layers include silicon oxide layers.
 29. The semiconductor device of claim 26 further comprising third element isolation layers that contact both side surfaces of the second element isolation layers, and have top surfaces higher than the top surfaces of the active regions.
 30. The semiconductor device of claim 29, wherein the second element isolation layers and the third element isolation layers are alternately disposed along the direction of the predetermined angle with respect to the first direction.
 31. The semiconductor device of claim 26, wherein the first element isolation layers contact the second element isolation layers.
 32. The semiconductor device of claim 26, wherein the gate electrode extends at a transverse angle with respect to the first direction.
 33. A method of manufacturing a semiconductor device having vertical channels, the method comprising: forming element isolation layers in etched recesses in a semiconductor substrate to define a plurality of active regions; forming mask layers on the active regions; forming a first mask pattern, the first mask pattern formed in stripes oriented in a first direction to cover at least a portion between adjacent active regions; forming a second mask pattern, the second mask pattern formed in stripes oriented in a second direction transverse from the first direction; removing a portion of the exposed element isolation layers using the first and second mask patterns as etching masks to expose at least a portion of the sidewalls of the active regions; removing the first and second mask patterns; and forming gate electrodes on the exposed active regions.
 34. The method of claim 33, further comprising removing the mask layers on the active layer before forming the gate electrodes.
 35. The method of claim 33, wherein the mask layers include a pad oxide layer and a pad nitride layer.
 36. The method of claim 33, wherein forming element isolation layers comprises: forming sidewall oxide layers on sidewalls of the recessed regions; forming a nitride layer liner which covers exposed portions of the sidewall oxide layers and the mask layer; and filling the recessed regions with a filling material layer.
 37. The method of claim 33, further comprising forming gate insulation layers to cover the exposed surfaces of the active region before forming the gate electrodes. 